其它 其它 注塑 | |
用于机械零件、消费用品等 | |
特性:改进机器进料和脱模特性。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM|1.2 | % |
吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 50%RH|- | % |
吸水率 | 饱和(23℃) | ASTM D-570 | DAM|8.5 | % |
吸水率 | 饱和(23℃) | 50%RH|- | % | |
比重 | ASTM D-792 | DAM|1.14 | ||
比重 | ASTM D-792 | 50%RH|1.14 | ||
泰伯磨耗量 | cs-17 Wheel,1000g | DAM|- | mg/1000 cycles | |
泰伯磨耗量 | cs-17 Wheel,1000g | 50%RH|7 | mg/1000 cycles | |
埃佐冲击强度 | 23℃ | ASTM D-256 | DAM|53 | j/m |
埃佐冲击强度 | 23℃ | ASTM D-256 | 50%RH|112 | j/m |
洛氏硬度M | ASTM D-785 | DAM|M79 | ||
洛氏硬度M | ASTM D-785 | 50%RH|M59 | ||
硬度计硬度 | ASTM D-676 | DAM|89 | ||
硬度计硬度 | ASTM D-676 | 50%RH|82 | ||
洛氏硬度R | ASTM D-785 | DAM|R121 | ||
洛氏硬度R | ASTM D-785 | 50%RH|R108 | ||
屈服强度 | 23℃ | DAM|82.7 | MPa | |
屈服强度 | 23℃ | 50%RH|58.6 | MPa | |
拉伸强度 | 23℃ | ASTM D-638 | DAM|82.7 | MPa |
拉伸强度 | 23℃ | ASTM D-638 | 50%RH|77.2 | MPa |
揉曲模量 | 23℃ | ASTM D-790 | DAM|2827 | MPa |
揉曲模量 | 23℃ | ASTM D-790 | 50%RH|1207 | MPa |
拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM|157 | KJ/m2 |
拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | 50%RH|231 | KJ/m2 |
1%形变时的压应力 | ASTM D-695 | DAM|33.8 | MPa | |
1%形变时的压应力 | ASTM D-695 | 50%RH|- | MPa | |
剪切强度 | 23℃ | ASTM D-732 | DAM|66.2 | MPa |
剪切强度 | 23℃ | ASTM D-732 | 50%RH|- | MPa |
断裂伸长率 | 23℃ | ASTM D-638 | DAM|60 | % |
断裂伸长率 | 23℃ | ASTM D-638 | 50%RH|≥300 | % |
屈服伸长率 | ASTM D-638 | DAM|5 | % | |
屈服伸长率 | ASTM D-638 | 50%RH|25 | % | |
拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM|504 | KJ/m2 |
拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | 50%RH|1470 | KJ/m2 |
介电常数 | 106Hz(cps) | ASTM D-150 | DAM|3.6 | |
介电常数 | 106Hz(cps) | ASTM D-150 | 50%RH|4.6 | |
耗散因数 | 100Hz(cps) | ASTM D-150 | DAM|0.01 | |
耗散因数 | 100Hz(cps) | ASTM D-150 | 50%RH|0.2 | |
介电常数 | 103Hz(cps) | ASTM D-150 | DAM|3.9 | |
介电常数 | 103Hz(cps) | ASTM D-150 | 50%RH|7.0 | |
耗散因数 | 106Hz(cps) | ASTM D-150 | DAM|0.02 | |
耗散因数 | 106Hz(cps) | ASTM D-150 | 50%RH|0.1 | |
耗散因数 | 103Hz(cps) | ASTM D-150 | DAM|0.02 | |
耗散因数 | 103Hz(cps) | ASTM D-150 | 50%RH|0.2 | |
体积电阻率 | ASTM D-257 | DAM|1015 | Ω.cm | |
体积电阻率 | ASTM D-257 | 50%RH|1013 | Ω.cm | |
介电常数 | 100Hz(cps) | ASTM D-150 | DAM|4.0 | |
介电常数 | 100Hz(cps) | ASTM D-150 | 50%RH|8.0 | |
荷重形变 | 13.8MPa,50℃ | ASTM D-621 | DAM|1.4 | % |
荷重形变 | 13.8MPa,50℃ | ASTM D-621 | 50%RH|- | % |
热畸变温度 | 18×106Pa | ASTM D-648 | DAM|90 | ℃ |
热畸变温度 | 18×106Pa | ASTM D-648 | 50%RH|- | ℃ |
熔点结晶 | ASTM D-2177 | DAM|270 | ℃ | |
熔点结晶 | ASTM D-2177 | 50%RH|- | ℃ | |
UL可燃性导级 | UL 94 | DAM|94 | ||
UL可燃性导级 | UL 94 | 50%RH|V-2 | ||
脆化温度 | ASTM D-746 | DAM|-80 | ℃ | |
脆化温度 | ASTM D-746 | 50%RH|-65 | ℃ |
PA66 101L塑料供应商,长期销售新加坡杜邦生产的PA66原料,以上是“PA66 101L”塑胶料的物性表参数.近期代理商可转仓交易:
● PA66 德国Melos NA40 GR30 NL IH
改良抗撞击性、抗撞击性,良好、良好的电气性能、韧性良好、中等硬度
● PA66 普利朗 PA880
超高抗冲击性
● PA66 南京立汉 A102
流动性高, 脱模性能良好, 一般目的
● PA66 德国爱彼斯 ALCOM PA66 910/1 GF30 MO1
填料:玻璃纤维增强材料, 30% 填料按重量。
● PA66 德国CP WELLAMID Nylon 6600/42 HWCP
冲击改性,热稳定性