性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.13 | g/cm3 | |
密度 | ISO1183 | 1.13 | g/cm3 | |
收缩率-流动(3.18mm) | 0.90 | % | ||
吸水率(24hr) | ASTMD570 | 1.6 | % | |
吸水率(23°C,24hr) | ISO62 | 1.6 | % | |
吸水率(饱和) | ASTMD570 | 9.3 | % | |
吸水率(饱和,23°C) | ISO62 | 9.3 | % | |
WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.6 | % | |
吸水率(平衡,23°C,50%RH) | ISO62 | 2.6 | % | |
拉伸模量(23°C) | ISO527-2 | 3500 | MPa | |
抗张强度 | 屈服,-40°C | ASTMD638 | 137 | MPa |
抗张强度 | 屈服,23°C | ASTMD638 | 90.0 | MPa |
抗张强度 | 屈服,80°C | ASTMD638 | 40.0 | MPa |
抗张强度 | Yield,121°C | ASTMD638 | 30.0 | MPa |
拉伸应力(屈服,23°C) | ISO527-2 | 85.0 | MPa | |
抗张强度 | 断裂,-40°C | ASTMD638 | 130 | MPa |
抗张强度 | 断裂,23°C | ASTMD638 | 90.0 | MPa |
抗张强度 | 断裂,80°C | ASTMD638 | 35.0 | MPa |
抗张强度 | Break,121°C | ASTMD638 | 25.0 | MPa |
伸长率 | 屈服,-40°C | ASTMD638 | 3.0 | % |
伸长率 | 屈服,23°C | ASTMD638 | 4.0 | % |
伸长率 | 屈服,80°C | ASTMD638 | 25 | % |
伸长率 | Yield,121°C | ASTMD638 | 27 | % |
拉伸应变(屈服,23°C) | ISO527-2 | 4.0 | % | |
伸长率 | 断裂,-40°C | ASTMD638 | 5.0 | % |
伸长率 | 断裂,23°C | ASTMD638 | 12 | % |
伸长率 | 断裂,80°C | ASTMD638 | >100 | % |
伸长率 | Break,121°C | ASTMD638 | >100 | % |
标称拉伸断裂应变(23°C) | ISO527-2 | 10 | % | |
弯曲模量 | -40°C | ASTMD790 | 3370 | MPa |
弯曲模量 | 23°C | ASTMD790 | 3170 | MPa |
弯曲模量 | 65°C | ASTMD790 | 600 | MPa |
弯曲模量 | 90°C | ASTMD790 | 440 | MPa |
弯曲模量 | 121°C | ASTMD790 | 385 | MPa |
弯曲模量(23°C) | ISO178 | 2800 | MPa | |
弯曲强度 | -40°C | ASTMD790 | 183 | MPa |
弯曲强度 | 23°C | ASTMD790 | 110 | MPa |
弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa |
弯曲强度 | 121°C | ASTMD790 | 21.0 | MPa |
弯曲应力(23°C) | ISO178 | 95.0 | MPa | |
简支梁缺口冲击强度(23°C) | ISO179 | 3.0 | kJ/m2 | |
简支梁无缺口冲击强度(23°C) | ISO179 | NoBreak | ||
悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 32 | J/m |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 48 | J/m |
洛氏硬度(R级) | ASTMD785 | 120 | ||
球压硬度 | ISO2039-1 | 200 | MPa | |
载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 190 | °C | |
热变形温度(0.45MPa,未退火) | ISO75-2/B | 160 | °C | |
载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 75.0 | °C | |
热变形温度(1.8MPa,未退火) | ISO75-2/A | 60.0 | °C | |
熔融峰值温度 | ASTMD3418 | 220 | °C | |
溶融温度(DSC) | ISO3146 | 220 | °C | |
线形热膨胀系数-流动 | ASTME831 | 8.1E-5 | cm/cm/°C | |
RTIElec | 0.71mm | UL746 | 130 | °C |
RTIElec | 1.5mm | UL746 | 130 | °C |
RTIElec | 3.0mm | UL746 | 130 | °C |
RTIElec | 6.0mm | UL746 | 130 | °C |
RTIImp | 0.71mm | UL746 | 95.0 | °C |
RTIImp | 1.5mm | UL746 | 105 | °C |
RTIImp | 3.0mm | UL746 | 105 | °C |
RTIImp | 6.0mm | UL746 | 105 | °C |
RTIStr | 0.71mm | UL746 | 95.0 | °C |
RTIStr | 1.5mm | UL746 | 105 | °C |
PA6 8202C HS BK-102塑料供应商,长期销售德国巴斯夫生产的PA6原料,以上是“PA6 Ultramid® 8202C HS BK-102”塑胶料的物性表参数.近期代理商可转仓交易:德国朗盛 PA6 Durethan® BG 30 FN05 000000
美国NOVA PC NOVA PC 1043 C2 注射成型
沙伯基础 PC LEXAN™ EXL1434 resin
沙伯基础 PC LEXAN™ EXL1463T resin
美国Delta PA66 Delta N66 UT
美国Polymer Resources PBT PRL TPSF-G30 填料,玻璃纤维增强材料,30%填料按重量.结构泡沫
美国RTP PBT RTP 1000 UV 抗紫外线性能良好,注射成型
美国RTP PBT RTP 1005 填料,玻璃纤维增强材料,30%填料按重量.
德国巴斯夫 PBT Ultradur® B 4040 G10 BK05110
中国南京聚隆科技 PA66 Wondel® A AM3 填料,中国南京聚隆科技.
意大利Vamp Tech PA66 DENILUB PA66 NEAT RESIN
沙伯基础 PA66 LNP™ THERMOCOMP™ RX96592 compound 填料,专有填料.
美国杜邦 PA66 Zytel® FR70M30V0 BK010 填料,矿物填料,30%填料按重量.
意大利拉题 PA66 Latamid 66 H2 K/50 填料,碳纤维增强材料,50%填料按重量.
日本尤尼吉可 PA6 UNITIKA Nylon 6 EX-1030 抗撞击性高 电器外壳,汽车的发动机罩下的零件,汽车领域的应用,汽车电子,建筑应用领域
● PA6 德国开德阜 AKROMID B3 GF 35 natural (2473)
填料:玻璃纤维增强材料, 35% 填料按重量。
● PA6 德国Kunststoff GERMAMID 6 HZ 4
抗撞击性高
● PA6 巴西Petropol PA B3 G20 PRTA011 NT307 MSP
玻璃纤维增强材料20% 填料按重量、良好的电气性能
● PA6 中国南京鸿锐塑料 Nanjing Hongrui PA6 B3010
填料:玻璃纤维增强材料, 50% 填料按重量。
● PA6 波兰ZAT T-27GB30
玻璃珠增强,注塑