沙伯基础 PEI ULTEM™ AR9100 resin
- PEI ULTEM™ AR9100 resin 应用
-
- 沙伯基础 PEI ULTEM™ AR9100 resin 物理特性
-
性能项目 试验条件[状态] 测试方法 测试数据 比重 ASTMD792 1.32 g/cm3 熔流率（熔体流动速率）(337°C/6.6kg) ASTMD1238 6.9 g/10min 收缩率-流动(3.20mm) InternalMethod 0.50to0.60 % 拉伸模量2 ASTMD638 4340 MPa 抗张强度3(屈服) ASTMD638 110 MPa 抗张强度3(断裂) ASTMD638 120 MPa 伸长率4(断裂) ASTMD638 8.0 % FlexuralModulus4(100mmSpan) ASTMD790 5030 MPa FlexuralStrength4(Yield,100mmSpan) ASTMD790 193 MPa 悬壁梁缺口冲击强度(23°C) ASTMD256 69 J/m ReverseNotchIzodImpact(3.20mm) ASTMD256 480 J/m 载荷下热变形温度(1.8MPa,未退火,6.40mm) ASTMD648 208 °C FAAFlammability5 FAR25.853 NATURAL NBSSmokeDensity Flaming,Dmax ASTME662 5.00 NBSSmokeDensity Flaming,Ds,1.5min ASTME662 0.00 NBSSmokeDensity Flaming,Ds,4min ASTME662 5.00 OSU峰值放热速率6 FAR25.853 40.0 kW/m2 OSU总放热量7 FAR25.853 5.00 kWmin/m2 VerticalBurnTest Testa(60s),passesat FAR25.853 0.0 hr VerticalBurnTest Testb(12s),passesat FAR25.853 0.0 hr
PEI AR9100 resin塑料供应商,长期销售沙伯基础生产的PEI原料,以上是“PEI ULTEM™ AR9100 resin”塑胶料的物性表参数.近期代理商可转仓交易：荷兰Purac PLA Purac PLA Blend A
日本三菱 TPV Trexprene® A64BU
美国APS TPV Viprene™ G75A-32U-NAT 抗紫外线性能良好,良好的流动性,热稳定性,挤出,注射成型
美国Teknor Apex TPE Telcar® DE 6052 挤出,注射成型 插头,柔软的把手,减震衬垫,把手,玩具
美国Star TPE StarPet® 8070-1007
台湾大东 TPU聚脂 ISOTHANE® 1085A-FR
德国凯柏胶宝 TPE THERMOLAST® K TP9CDZ (Series: EX)
台湾丰炬工业 SEBS PHOENIX™ 2451
台湾定欣 SEBS DIOSHY® SP-595W
意大利Versalis EVA Greenflex® ML 21 F 共聚物,良好的柔韧性,食品接触的合规性,高ESCR,抗应力开裂,注射成型
德国莱曼 PPS LUVOCOM® 1301-8517 填料,碳纤维增强材料.汽车领域的应用,工程配件,商务设备,医疗/护理用品,纺织应用
沙伯基础 PEI LNP™ VERTON™ EV008 compound 填料,长玻璃纤维,40%填料按重量.构件
日本旭化成 POM均聚 Tenac™ 5050 中等粘性,均聚物,快的成型周期,低翘曲性 工程配件,外壳,通用,齿轮
美国Rochling POM共聚 SUSTARIN® C FG 耐化学性良好,食品接触的合规性,尺寸稳定性良好 非特定食品应用
以色列普利朗 POM共聚 RAMTAL PM3007G6 填料,玻璃纤维增强材料,30%填料按重量.
- 相关产品
● PEI 美国RJM RJM EX002F1
填料：碳纤维增强材料。
● PEI 美国RTP RTP 2185 TFE 5
填料：碳纤维增强材料, 30% 填料按重量。
● PEI 沙伯基础 ULTEM 1010R resin
● PEI 美国RTP ESD A 2180 EM
静电放电保护，静态导电，良好的成型性能
● PEI 沙伯基础 ULTEM 1285 resin